The behavior of high-performance concrete (HPC) at high temperatures is very complex and also affects the global behavior of heated HPC-based structures. Researchers have also reported how various types of fibers affected the mechanical properties of cement-based materials at high temperatures. This study aims to discuss the effects of high temperatures on the compressive strength and elastic modulus of HPC with polypropylene (PP) and jute fiber.

Adding synthetic fiber (especially the PP type) to HPC is a widely used and effective method of preventing explosive spalling. Although researchers have experimentally determined the permeability of heated PP-fiber-reinforced HPC, few studies have investigated how adding natural fiber such as jute to this type of concrete might prevent spalling. In this study, the effects of high temperatures on the compressive strength and elastic modulus of HPC with PP and jute fiber (jute fiber addition ratio: 0.075 vol.%; length: 12 mm; PP fiber addition ratio: 0.075 vol.%; length: 12 mm) were experimentally investigated.

The work was intended to clarify the influence of elevated temperatures ranging from 20°C to 500°C on the material mechanical properties of HPC at 80 MPa. HSC with jute fiber showed a compressive strength loss of about 40 per cent at 100°C before recovering to full strength between 200°C and 300°C.

The elastic modulus of high-strength concrete decreased by 10-40 per cent between 100°C and 300°C. At 500°C, the elastic modulus was only 30 per cent of the room temperature value. The thermal expansion strain of all specimens was 0.006 at 500°C.

This study aims to investigate the effect of high temperature (600°C) on the compressive strength of concrete covered with a mixture of polypropylene fiber and gypsum plaster (PFGP).

To study the compressive strength of concrete specimens exposed to temperature, 16 cubic specimens (size: 150 mm × 150 mm × 150 mm) were made. After 28 days of processing and gaining the required strength of specimens, first, polypropylene fiber was mixed with gypsum plaster (CaSO4.2H2O) and then the concrete specimens were covered with this mixture. To cover the concrete specimens with the PFGP, the used PFGP thickness was 15 mm or 25 mm. The polypropylene rates mixed with the gypsum plaster were 1, 3 and 5 per cent. A total of 14 specimens, 12 of which were covered with PFGP, were exposed to high temperature in two target times of 90 and 180 min.

The results show that the PFGP as covering materials can improve the compressive strength lost because of the heating of the concrete specimens. The results also show that the presence of polypropylene fiber in gypsum plaster has the effect on the compressive strength lost because of the heating of the PFGP-covered concrete. The cover of PFGP having 3 per cent polypropylene fiber had the best effect on remained strength of the specimens.

The cover of PFGP having 3 per cent polypropylene fiber has the best effect on remained strength of the PFGP covered specimens exposed to temperature.